Elastollan® C60A10W

热塑性聚氨酯弹性体（聚酯）

BASF Corp. Thermoplastic Polyurethanes

Technical Data

产品说明

Elastollan® C60A10W is a polyester-based thermoplastic polyurethane (TPU) containing a plasticizer. It exhibits excellent abrasion resistance and toughness, good hydrolytic stability, good heat, oil, fuel, and solvent resistance. As with all TPU products, Elastollan C60A10W must be dried before processing. The drying step is required to both dry the granules and also maintain a low moisture content until the product enters the processing equipment. The water content must be less than 0.03% before processing. The typical drying conditions should be 2-4 hours @ 160°-180°F (70°-85°C). Elastollan C60A10W (or LP9101) can be stored for up to 1 year in its original container. Containers should be stored in a cool and dry area.

总体

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet (English)

搜索 UL 黄卡 • BASF Corp. Thermoplastic Polyurethanes

• Elastollan®

供货地区 • 北美洲

• 经增塑 • 耐热性，高 • 韧性良好

性能特点 • 抗溶解性 • 耐油

• 水解稳定

• 耐磨蚀性，良好 • 耐油性能

形式 • 颗粒

加工方法 • 挤出

物理性能额定值单位制测试方法

比重 1.14g/cm³ ASTM D792

弹性体额定值单位制测试方法

拉伸应力 ASTM D412

100%应变 2.55MPa

300%应变 4.69MPa

抗张强度 (断裂) 22.8MPa ASTM D412

伸长率 (断裂) 870% ASTM D412

断裂伸长率 75% ASTM D412

撕裂强度 3 52.5kN/m ASTM D624

压缩永久变形 ASTM D395B

23°C, 22.0 hr 20%

70°C, 22.0 hr 45%

硬度额定值单位制测试方法

硬度计硬度 (邵氏 A) 63 ASTM D2240

注射额定值单位制

干燥温度 71.1 到 82.2°C

干燥时间 2.0 到 4.0hr

建议的最大水分含量 0.030%

加工（熔体）温度 163 到 182°C

挤出额定值单位制

干燥温度 71.1 到 82.2°C

干燥时间 2.0 到 4.0hr

建议的最大水分含量 0.030%

熔体温度 160 到 179°C