Texin® HM-1206
热塑性聚氨酯弹性体（聚醚）
Bayer MaterialScience LLC - PUR
Technical Data
产品说明
Texin HM-1206 resin is a clear, high performance thermoplastic polyurethane which possesses the stiffness and modulus of standard engineering thermoplastics. This resin exhibits excellent heat and chemical resistance. It also has very good impact resistance relative to thermoplastics such as polystyrene, polymethylmethacrylate, and styrene-acryonitrile. Other key attributes of Texin HM-1206 include low moisture absorption, low mold shrinkage, a low coefficient of thermal expansion, and good abrasion resistance. It can be processed by injection molding or extrusion.
Typical applications include fuel bowls, compressed air filter bowls, sight glasses and level indicators. As with any product, use of Texin HM-1206 resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
总体
材料状态 • 已商用：当前有效
• Processing - Extrusion (English)
资料 1 • Processing - Injection Molding (English)
• Technical Datasheet (English)
搜索 UL 黄卡 • Bayer MaterialScience LLC - PUR
• Texin®
供货地区 • 北美洲
• 刚性，良好 • 耐磨蚀性，良好 • 吸潮性差
性能特点 • 抗撞击性，良好 • 耐热性，高
• 耐化学性良好 • 收缩性低
用途 • 光学应用 • 容器 • 眼镜
RoHS 合规性 • RoHS 合规
外观 • 清晰/透明
形式 • 颗粒料
加工方法 • 挤出 • 注射成型
物理性能 额定值单位制 测试方法
比重
-- 1.24g/cm³ ASTM D792
-- 1.25g/cm³ ISO 1183
收缩率
流动 0.50% ASTM D955
流量 0.50% ISO 294-4
吸水率
饱和 0.17% ASTM D570
饱和, 23°C 0.17% ISO 62
机械性能 额定值单位制 测试方法
拉伸模量 2330MPa ASTM D638
抗张强度 ASTM D638
屈服 76.5MPa
断裂 61.4MPa
伸长率 ASTM D638
屈服 7.8%
断裂 170%
弯曲模量 ASTM D790
-- 2340MPa ISO 178
-- 3 103MPa
弯曲强度 110MPa ASTM D790
ISO 178
抗泰伯磨耗
1000 Cycles, 1000 g, H-18 转轮 39.0mg ISO 4649
1000 Cycles, 1000 g, H-18 转轮 39.0mg ASTM D1044
Texin® HM-1206
热塑性聚氨酯弹性体（聚醚）
Bayer MaterialScience LLC - PUR
机械性能 额定值单位制 测试方法
Flexural Strain at Flexural Strength
-- 7.0% ISO 178
-- 7.0% ASTM D790
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 (23°C, 3.18 mm) 390J/m ASTM D256
无缺口悬臂梁冲击
-30°C, 3.18 mm 4000J/m ASTM D256
23°C, 3.18 mm 4 3800J/m ASTM D4812
硬度 额定值单位制 测试方法
洛氏硬度 ASTM D785
M 计秤 87
R 计秤 125
热性能 额定值单位制 测试方法
热变形温度 ASTM D648
0.45 MPa, 未退火, 3.18 mm 92.2°C
0.45 MPa, 退火, 3.18 mm 97.8°C
1.8 MPa, 未退火, 3.18 mm 76.7°C
1.8 MPa, 退火, 3.18 mm 88.9°C
维卡软化温度
-- 5 53.3°C ASTM D1525 6
-- 7 43.3°C ASTM D1525 6
-- 5 128°C ISO 306/A50
-- 7 110°C ISO 306/A50
线形膨胀系数 - 流动 0.000065cm/cm/°C ASTM D696
光学性能 额定值单位制 测试方法
折射率 1.605 ASTM D542
透射率
3.18 µm 90.0% ISO 3583
3180 µm 90.0% ASTM D1003
雾度
3180 µm 3.0% ISO 3583
3180 µm 3.0% ASTM D1003
注射 额定值单位制
干燥温度 104 到 121°C
干燥时间 4.0hr
建议的最大水分含量 < 0.030%
建议的最大回制料比例 20%
螺筒后部温度 235 到 236°C
螺筒中部温度 238 到 249°C
螺筒前部温度 238 到 249°C
射嘴温度 243 到 254°C
加工（熔体）温度 235 到 250°C
模具温度 43.3 到 65.6°C
注塑温度 41.4 到 96.5MPa
注射速度 中等
背压 < 5.52MPa
螺杆转速 40 到 80rpm
垫层 15.9mm
注射说明
Hold Pressure: 60 to 80% of Injection Pressure
挤出 额定值单位制
干燥温度 104 到 121°C
Texin® HM-1206
热塑性聚氨酯弹性体（聚醚）
Bayer MaterialScience LLC - PUR
挤出 额定值单位制
干燥时间 4.0hr
建议的最大水分含量 < 0.030%
第1气缸区温度 225 到 250°C
第2气缸区温度 225 到 240°C
第3气缸区温度 225 到 240°C
熔体温度 230°C
模具温度 230 到 240°C