Elastollan® 1185A10FHF    
    
热塑性聚氨酯弹性体（聚醚）    
    
BASF Corp. Thermoplastic Polyurethanes   
     
 Technical Data    
     

产品说明

Elastollan® 1185A10FHF is a polyether-based thermoplastic polyurethane (TPU) containing a non-halogenated fire retardant. It is specifically formulated for wire and cable jacketing, extruded profile, sheet and film applications. It exhibits excellent abrasion resistance, toughness, low temperature properties, hydrolytic stability and fungus resistance. Elastollan® 1185A10FHF is formulated to exhibit the flame retardancy characteristics as described in the table below. As with all TPU products, Elastollan® 1185A10FHF must be dried before processing. The drying step is required to both dry the granules and also maintain a low moisture content until the product enters the processing equipment. The water content must be less than 0.03% before processing. The typical drying conditions should be 2-4 hours @ 175°-195°F (80°-90°C). Elastollan® 1185A10FHF can be stored for up to 1 year in its original container. Containers should be stored in a cool and dry area.

总体

材料状态 • 已商用：当前有效   
资料 1 •  Technical Datasheet (English)
  
搜索 UL 黄卡 •  BASF Corp. Thermoplastic Polyurethanes
 
 •  Elastollan®
  
    
供货地区 • 北美洲   
添加剂 • 阻燃   
性能特点 • 低温韧性 • 耐磨蚀性，良好 • 阻燃性能 
 • 抗菌性 • 水解稳定  
    
用途 • 薄膜 • 电线护套 • 型材 
 • 电缆护套 • 片材  
    
外观 • 清晰/透明   
形式 • 颗粒料   
加工方法 • 挤出 • 注射成型  

物理性能 额定值单位制 测试方法
比重 1.23g/cm³ ASTM D792
机械性能 额定值单位制 测试方法
拉伸模量 26.2MPa ASTM D638
弯曲模量 48.3MPa ASTM D790
抗泰伯磨耗 (1000 g, H-18 转轮) 100mg ASTM D1044
弹性体 额定值单位制 测试方法
拉伸应力  ASTM D412
100%应变 10.7MPa 
300%应变 17.9MPa 
抗张强度 (断裂) 36.5MPa ASTM D412
伸长率 (断裂) 500% ASTM D412
撕裂强度 3 96.3kN/m ASTM D624
压缩永久变形  ASTM D395B
23°C, 22.0 hr 25% 
70°C, 22.0 hr 45% 
硬度 额定值单位制 测试方法
硬度计硬度 (邵氏 A) 88 ASTM D2240
热性能 额定值单位制 测试方法
玻璃转化温度(DSC) -40.0°C DSC
维卡软化温度 72.2°C ASTM D1525
可燃性 额定值单位制 测试方法
UL 阻燃等级  UL 94
1.52 mm V-2 
3.05 mm V-0 
极限氧指数 25% ASTM D2863

 
Elastollan® 1185A10FHF
热塑性聚氨酯弹性体（聚醚）
BASF Corp. Thermoplastic Polyurethanes 

补充信息
DIN Abrasion Resistance, DIN 53516: 35 mm³ loss
The value listed as Tensile Modulus ASTM D638, was tested in accordance with E-Modulus ASTM D412.

注射 额定值单位制
干燥温度 79.4 到 90.6°C
干燥时间 2.0 到 4.0hr
建议的最大水分含量 0.030%
加工（熔体）温度 182 到 204°C
挤出 额定值单位制
干燥温度 79.4 到 90.6°C
干燥时间 2.0 到 4.0hr
建议的最大水分含量 0.030%
熔体温度 182 到 204°C

备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。

2 一般属性：这些不能被视为规格。

3 C 模具