Bayflex® 1212    
    
热塑性聚氨酯弹性体（聚醚）    
    
Bayer MaterialScience LLC   
     
 Technical Data    
     

产品说明

Texin 1212 resin is an aromatic polyether-based thermoplastic polyurethane with a Shore hardness of appoximately 60D. Texin 1212 can be processed by injection molding, extrusion, or blow molding and its characterized by a low gel content, good clarity and abrasion resistance, and very good chemical resistance to oils, solvents, and other non-aqueous solutions.

Textin 1212 natural color resin complies with FDA food-contact regulations 21 CFR 177.1680 (Polyurethane Resins) and 177.2600 (Rubber Articles Intended for Repeated Use), subject to the limitations of these and any other applicable regulations. Texin 1212 has a wide processing window, which allows for ease of film and sheet production. Typical applications include belting, hose, cable jackets, hose jackets, athletic shoes, film, tubing and extended profiles. As with any product, use of Text 1212 resin in any given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.

总体

 材料状态  • 已商用：当前有效   
 资料 1  •  Technical Datasheet (English)
  
 搜索 UL 黄卡 •  Bayer MaterialScience LLC
  
  •  Bayflex®
  
      
 供货地区  • 北美洲   
 性能特点  • 低速凝固晶点 • 耐磨蚀性，良好 • 中等透明度 
   • 耐化学性良好 • 食品接触的合规性  
      
   • 薄膜 • 管道 • 型材 
 用途  • 电缆护套 • 管道  
   • 非特定食品应用 • 鞋类  
 机构评级  • FDA 21 CFR 177.1680 • FDA 21 CFR 177.2600  
 加工方法  • 薄膜挤出 • 挤出 • 注射成型 
   • 吹塑成型 • 片材挤出成型  
      
      
 物理性能   额定值单位制 测试方法 
 比重     
--   1.23g/cm³ ASTM D792 
--   1.22g/cm³ ISO 1183 
 机械性能   额定值单位制 测试方法 
 弯曲模量    ASTM D790 
 23°C   165MPa ISO 178 
      
 70°C   50.3MPa  
 抗泰伯磨耗    
 1000 Cycles, 1000 g, H-18 转轮  60.0mg ISO 4649 
 1000 Cycles, 1000 g, H-18 转轮  60.0mg ASTM D3489 
 弹性体   额定值单位制 测试方法 
 拉伸应力    ASTM D412 
 100%应变  17.9MPa ISO 37 
     
 300%应变  32.4MPa  
 拉伸应力     
 断裂   44.8MPa ISO 37 
--   44.8MPa ASTM D412 
 伸长率 (断裂)  450% ASTM D412 
    ISO 37 
      
 撕裂强度 3  200kN/m ASTM D624 
     ISO 34-1 
      
 压缩永久变形 4   ASTM D395 
 23°C, 22.0 hr  16% ISO 815 
     
 70°C, 22.0 hr  43%  
 硬度   额定值单位制 测试方法 
 硬度计硬度 (邵氏 D)  60 ASTM D2240 
    ISO 868 
      
 
Bayflex® 1212       
热塑性聚氨酯弹性体（聚醚）       
       
Bayer MaterialScience LLC    
       
  热性能  额定值单位制 测试方法 
      
  玻璃转化温度  -7.22°C Internal Method 
  维卡软化温度  121°C ISO 306/A 
     ASTM D1525 5 
         
  注射  额定值单位制     
  螺筒后部温度 191 到 202°C     
  螺筒中部温度 193 到 207°C     
  螺筒前部温度 193 到 207°C     
  射嘴温度 196 到 213°C     
  加工（熔体）温度 196 到 207°C     
  模具温度 15.6 到 37.8°C     
  注塑温度 41.4 到 103MPa     
  注射速度  中等     
  背压  < 5.52MPa     
  螺杆转速 40 到 80rpm     
  垫层  < 3.18mm     
  注射说明       
  Holding Pressure: 60 to 80% of Injection Pressure       
  挤出  额定值单位制     
  第1气缸区温度 193 到 204°C     
  第3气缸区温度 193 到 204°C     
  第5气缸区温度 196 到 210°C     
  熔体温度 196 到 207°C     
  模具温度 196 到 210°C     

备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。

2 一般属性：这些不能被视为规格。

3 Die C

4 Post-Cured

5 标准 A (50°C/h)